high Silicon Manganese oxide powder for welding flux Mn 35%

high Silicon Manganese oxide powder for welding flux Mn 35%

    • high Silicon Manganese oxide powder for welding flux  Mn 35%
    • high Silicon Manganese oxide powder for welding flux  Mn 35%
    • high Silicon Manganese oxide powder for welding flux  Mn 35%
    • high Silicon Manganese oxide powder for welding flux  Mn 35%
    • high Silicon Manganese oxide powder for welding flux  Mn 35%
  • high Silicon Manganese oxide powder for welding flux  Mn 35%

    Product Details:

    Place of Origin: CHINA
    Brand Name: HJ
    Certification: ISO9001
    Model Number: 431

    Payment & Shipping Terms:

    Minimum Order Quantity: 5 metric tons
    Price: USD620
    Packaging Details: 25KG/BAG
    Delivery Time: 20 DAYS
    Payment Terms: T/T
    Supply Ability: 8000 METRIC TONS
    Contact Now
    Detailed Product Description

    High Silicon Manganese oxide Fused Flux HJ431 for Submerged arc welding flux

     

    High manganese oxide smelted welding flux / Fused Flux HJ431

    Executive Standards: GB/T 5293-2003 / F4A0-H08A;

    Equivalent to: JIS YSF42-W11;

    Equivalent to: AWS A5.17 F6AZ-EL12;

     

    Welding flux HJ431 is a kind of high manganese oxide and SiO2,CaF2 smelted flux.

    it is a kind of granule red brown to light yellow color;

    the size is about 2.5 ~ 4.0mm ( 8 mesh ~ 40mesh); and 1.5mm ~ 1.8mm ( 14mesh ~ 80 mesh );

    when used on AC or DC+. It is good at welding and weld-ability;

    Application of High Silicon manganese oxide selted flux:

    In combination with Welding wire EL12; EM12K; EH14. this conbination is suitable for welding LOW ALLOY STEEL, HIGH STRENGTH STEEL(  16Mn, 15MnVN) , the important structures, the fabrication of ships, boilers and pressure vessels etc.

    The chemical of welding flux:

    Mn+SiO2:  74 ~ 82 %;  CaF2+CaO : 10 ~ 14 %; MgO + Al2O3 : 9 ~ 12 %; low S.P.

    The mechanical of welded metal:

    Yield Strength : 388 MPa;

    Tensile Strength: 500 MPa;

    Elongation: 30

    Usage of Guiding:

    Dry the flux at 250C for two hours before  used;

    Completely remove rust. oil and dirt from the proove surface prior to welding;

     

     

     

     

     

     